1. Seven production bases in China, equipping with strict quality inspection and comprehensive after-sales service and offerring professional solutions in time;
2. The world's first breakthrough in stainless steel five-foot wide five-continuous rolling technology;
3. The first stainless steel whole-roll water plating black titanium and whole-roll vacuum plating color coil;
4. Annual output value of up to 5 million tons, can meet the product customization of more than 60 countries;
5. The final payment will be determined base on the actual weight.
5. Grade: 200/300/400;
6. Standard: QB/GB/ASTM/JIS/EN
| Commodity | Austenitic, Ferritic, Martensitic, Duplex, Cold rolled, Hot rolled |
| Grade | 201, 202, 301, 304, 304j1, 304l, 321, 309s, 310s, 2205, 409l, 410, 410s, 420, 420j1, 420j2, 430, 439, 409l, 443, 444, etc |
| Standard | ISO, JIS, ASTM, AS, EN, GB |
| Surface | N0.1, N0.2, N0.3, N0.4, N0.5, N0.6, N0.7, N0.8, 2D, 2B, 2BA,HL, BA,Mirror,6K, 8K, etc |
| Size | Thickness: 0.20-2.00mm or as customer's request
Width: 1000mm/1219mm/1240mm/1500mm or as customer's requirements
lnner Diameter(mm): 508/610
|
| MOQ | 5 ton |
| Packaging | Using wooden skids, VCI film, and wooden boards for packing to provide better protection and to prevent water and moisture |
| Trade Term | FOB, EXW, CIF |
| Transport Type | Container, bulk and sea |
| Delivery time | 25-35 days after confirmed order |
Chemical composition
| Grade | C(Max) | Mn(Max) | P(Max) | S(Max) | Si(Max) | Cr | Ni | Mo | N(Max) | Cu/Others |
| 304 | 0.08 | 2.00 | 0.045 | 0.030 | 1.000 | 18.00-20.00 | 8.00-10.50 | - | 0.10 | - |
| 304L | 0.030 | 2.00 | 0.045 | 0.030 | 1.000 | 18.00-20.00 | 8.00-12.00 | - | 0.10 | - |
| 310S | 0.08 | 2.00 | 0.045 | 0.030 | 1.500 | 24.00-26.00 | 19.00-22.00 | - | - | - |
| 316 | 0.080 | 2.00 | 0.045 | 0.030 | 1.000 | 16.00-18.00 | 10.00-14.00 | 2.00-3.00 | - | - |
| 316L | 0.030 | 2.00 | 0.045 | 0.030 | 1.000 | 16.00-18.00 | 10.00-14.00 | 2.00-3.00 | 0.10 | - |
| 409 | 0.08 | 1.00 | 0.040 | 0.010 | 1.000 | 10.50-11.75 | 0.50 | - | - | Ti=6x(C+N) |
| 430 | 0.12 | 1.00 | 0.040 | 0.030 | 1.000 | 16.00-18.00 | 0.75 | - | - | - |
| Surface | Characteristic | Processing Technology |
| N0.1 | Original | Pickled after hot rolling |
| 2D | Blunt | Hot rolling + annealing shot peening pickling + cold rolling + annealing pickling |
| 2B | Blurred | Hot rolling + annealing shot peening pickling + cold rolling + annealing pickling + tempering rolling |
| N0.3 | Matte | Polishing and tempering rolling with 100-120 mesh abrasive materials |
| N0.4 | Matte | Polishing and tempering rolling with 150-180 mesh abrasive materials |
| HL | Brushed | Grind the surface of the steel belt with an appropriate grinding grain size to make it show a certain longitudinal texture |
| BA | Bright | The surface is annealed and shows high reflectivity |
| 6K | Mirror | Rough grinding and polishing |
| 8K | Mirror | Fine grinding and polishing |